| GLASS | THE THICKNESS OF THE MATERIAL | LOWEST PUBLISHED | ESTIMATED NM POINT | ESTIMATED NM POINT | LAST PUBLISHED | ||||||||||
| GENERIC CODE | ORIGIN | THE GENERAL | SOURCE | AVAILABILITY | USED TO GENERATE THE PUBLISHED | TRANSMISSION OCCURRING | WHERE TRANSMISSION | WHERE TRANSMISSION | TRANSMISSION IN | ||||||
| ----- | ------ | ALPHA CODE USED | CATALOG | ------ | NM TRANSMISSION VALUES | IN OR NEAR | APPROACHES "~" 50% | APPROACHES "~" 90% | THE IR SPECTRUM THAT | KNOOP | YIELD | EXPANSION | DENSITY | DENSITY | |
| PER | MANUFACTURER OR | IN THE COUNTRY | DATE | P=PREFERRED/AVAIL. | PROVIDED ON THE | THE UV SPECTRUM | IS 90% OR GREATER | HARDNESS | (DEFORMATION) | COEFFICIENT | GM/CM^3 | LB./IN^3 | |||
| MIL-STD. | COUNTRY | INDICATED OR | FOR THE | EG=ECOLOGICAL | THE REFERENCED LINE | ----- | ----- | ----- | (SEE MFTR. | TEMPERATURE | ( X 10^-7) | ||||
| G-174-B | ------ | AS THE | LINE | H = HISTORICAL | ----- | ----- | ASCENDING FROM OR | ASCENDING FROM UV | DESCENDING FROM UV-VIS, | DESCRIPTION) | DEGREES C | -30 / +70 | |||
| INDICATED | I = INQUIRY | EXCEPTION: "*" INDICATES THAT | "~<"= 1% TRANSMISSION | NEAR THE UV REGION | REGION | & NEAR-IR REGIONS | |||||||||
| ----- | (SEE MFTR. | MANUFACTURER'S | ----- | NA = NOT AVAILABLE | THE VALUES WERE DERIVED FOR A | IS AT OR BELOW | ----- | ----- | ----- | DEGREES C | |||||
| MIL. CODE=NNNVVV | DESCRIPTION) | TRADEMARK | EXCEPTION: | ----- | HYPOTHETICAL 1MM THICK | NM POINT GIVEN | |||||||||
| ----- | CALCULATED | DERIVED = NOT | MATERIAL USING A | ----- | "~<"= 50% TRANS. PT. | "~<"= 90% TRANS. PT. | "~>"= 90% TRANS. PT. IS | ||||||||
| CONVERSION: | DERIVATION= | THE MANUFACTURER'S | LOGARITHM DENSITY FORMULA. | (XX%) TRANSMISSION | BELOW NM PT. GIVEN- | BELOW NM PT. GIVEN- | BEYOND NM PT. GIVEN- | ||||||||
| nd=1.+NNN | NOT FROM | PUBLISHED VALUES- | HOYA'S SOURCE DATA WAS USED | AT THE | (XX%) TRANS. AT THE | (XX%) TRANS. AT THE | (XX%) TRANS. AT THE | ||||||||
| vd=VV.V | A | HYPOTHETICAL | TO ILLUSTRATE THE THEORETICAL | NM POINT INDICATED | NM POINT INDICATED | NM POINT INDICATED | NM POINT INDICATED | ||||||||
| CATALOG | EFFECTS OF A THICKNESS CHANGE. | SEE | SEE | SEE | SEE | SEE | |||||||||
| *SEE DISCLAIMER* | *SEE DISCLAIMER* | *SEE DISCLAIMER* | *SEE DISCLAIMER* | *SEE DISCLAIMER* | *SEE DISCLAIMER* | *SEE DISCLAIMER* | *SEE DISCLAIMER* | *SEE DISCLAIMER* | *SEE DISCLAIMER* | DISCLAIMER | DISCLAIMER | DISCLAIMER | DISCLAIMER | DISCLAIMER | |
| 650337 | SCHOTT GLASS TECH. | SF17 | 1992 | H / I | 5MM | ~320nm | ~336nm | ~358nm | ~>2325.4nm (95.0%) | 350 | ----- | 85 | 3.87 | 0.140 | |
| 650384 | HAYWARD SCIENTIFIC | BF4 | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ||
| 650385 | RUSSIA | C245 | PRE 1992 | H / I | ----- | ----- | ----- | ----- | ----- | ----- | 63 | 3.86 | 0.140 | ||
| 650392 | CORNING-FRANCE | C51-39 | 1991 | P | 10MM | ~<330 (2.0%) | ~349 | ~380 | ~>1800 (97.8%) | ----- | 618 | 59 | 3.82 | 0.138 | |
| 650392 | SCHOTT GLASS TECH. | BaSF10 | 1992 | I | 5MM | ~<320 (3%) | ~338 | ~365.0 | ~>2325.4 (95.2%) | 400 | 635 | 86 | 3.91 | 0.142 | |
| 650393 | HOYA CORP. | BaFD10 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 460 | ------ | 3.81 | 0.138 | ||
| 650393 | HOYA CORP. | LaCL2 | 1998 | P | 5MM | ~<300 (21%) | ~315 | ~348 | ~>1550 (99.7%) | 580 | 69 | 3.74 | 0.135 | ||
| 650394 | OHARA CORP. | BAH30 | 1990 | I | 10MM | ~<330 (5%) | ~346 | ~383 | ~>1060 (99.5%) | 450 | 92 | 3.91 | 0.142 | ||
| 650557 | HOYA CORP. | LaCL2 | DERIVED | HYPOTHETICAL | 1MM* | ---- | ~<300 (72.5%) | ~321 | ~>1550 (99.9%) | 580 | 69 | 3.74 | 0.135 | ||
| 651308 | HOYA CORP. | ATF2 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 325 | 122 | 3.44 | 0.125 | ||
| 651383 | CHINA | ZBAF15 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 475 | 87 | 3.91 | 0.142 | ||
| 651383 | HOYA CORP. | BaFD4 | 1978 | H / I | 5MM | ~<340 (6%) | ~355 | ~375 | ~>700 (99.9%) | 485 | ----- | 3.80 | 0.138 | ||
| 651383 | OHARA CORP. | BAH24 | 1990 | H / I | 10MM | ~330 | ~352 | ~387 | ~>1060 (99.3%) | 440 | 86 | 3.91 | 0.142 | ||
| 651384 | EAST GERMANY | BaSF4 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~<340 (13.9%) | ~358 | ~400 | ~>1500 (99.4%) | ----- | 79 | 3.90 | 0.141 | ||
| 651419 | SCHOTT GLASS TECH. | BaSF57 | 1992 | I | 5MM | ~<350 (35%) | ~355 | ~378 | ~>2325.4 (96.1%) | 450 | ----- | 71 | 3.73 | 0.135 | |
| 651435 | RUSSIA | C390 | PRE 1992 | H / I | 10MM | ---- | ~<340 (55.0%) | ~390 | ~>1500 (97.7%) | ----- | 44 | 3.48 | 0.126 | ||
| 651558 | BAUSCH & LOMB | ----- | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | 3.81 | 0.138 | ||
| 651558 | HAYWARD SCIENTIFIC | DBC9 | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ||
| 651559 | CHINA | LAK10 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 475 | 61 | 3.81 | 0.138 | ||
| 651559 | CORNING-FRANCE | C51-56 | 1991 | P | 10MM | ~<320 (1.0%) | ~351 | ~385 | ~>1800 (98.5%) | ----- | 765 | 67 | 3.72 | 0.135 | |
| 651559 | SCHOTT GLASS TECH. | LaKN22 | 1992 | H / I | 5MM | ~<300 (11%) | ~324 | ~354 | ~>2325.4 (93%) | 510 | ----- | 66 | 3.73 | 0.135 | |
| 651559 | SCHOTT GLASS TECH. | NLAK22 | 2000 | P | 10MM | ~290 | ~325 | ~360 | ~>1970 (95.9%) | 600 | 66 | 3.73 | 0.135 | ||
| 651562 | HIKARI GLASS CO. | E-LAK04 | 2001 | EG/P | 10MM | --- | ---- | ---- | ---- | 612 | 678 | ----- | 3.26 | 0.118 | |
| 651562 | OHARA CORP. | LAL54 | 1990 | H / I | 10MM | ~<330 (7%) | ~346 | ~374 | ~>700 (99.6%) | 540 | 73 | 3.82 | 0.138 | ||
| 651562 | OHARA CORP. | LAL55 | 1990 | H / I | 10MM | ~<330 (2%) | ~348 | ~372 | ~>700 (99.7%) | 520 | 73 | 3.82 | 0.138 | ||
| 651562 | OHARA CORP. | S-LAL54 | 1996 | P/EG | 10MM | ~<330 (13%) | ~342 | ~367 | ~>2200 (91.3%) | 530 | 71 | 3.82 | 0.138 | ||
| 651584 | BAUSCH & LOMB | ----- | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | 3.75 | 0.136 | ||
| 652449 | HOYA CORP. | BaF23 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 500 | 81 | 4.79 | 0.173 | ||
| 652449 | SCHOTT GLASS TECH. | BaF51 | 1992 | I | 5MM | ~<350 (35%) | ~356 | ~382 | ~>2325.4 (92%) | 470 | 693 | 84 | 3.42 | 0.124 | |
| 652450 | SCHOTT GLASS TECH. | NBAF51 | 2000 | P/EG | 10MM | ~<350 (21%) | ~360 | ~387 | ~>1970 (95.0%) | 560 | 84 | 3.33 | 0.121 | ||
| 652584 | HOYA CORP. | LaC7 | DERIVED | HYPOTHETICAL | 1MM* | ----- | ~<290 (63.1%) | ~326 | ~>1550 (99.9%) | 580 | 69 | 3.62 | 0.131 | ||
| 652584 | HOYA CORP. | LaC7 | 1998 | P | 5MM | ~<280 (4%) | ~320 (50%) | ~355 | ~>1550 (99.5%) | 580 | 69 | 3.62 | 0.131 | ||
| 652585 | CORNING-FRANCE | C52-58 | 1991 | P | 10MM | ~<280 (2%) | ~334 | ~368 | ~>1800 (98.4%) | ----- | 729 | 69 | 3.60 | 0.130 | |
| 652585 | HIKARI GLASS CO. | E-LAK7 | 2001 | EG/P | 10MM | ~<280(5%) | ~309 | ~350 | ~>2000(95.7%) | ---- | 678 | ----- | 3.30 | 0.119 | |
| 652585 | OHARA CORP. | LAL7 | 1990 | H / I | 10MM | ~<280 (2%) | ~319 | ~355 | ~>700 (99.7%) | 560 | 67 | 3.73 | 0.135 | ||
| 652585 | OHARA CORP. | S-LAL7 | 1996 | P/EG | 10MM | ~<280 (9%) | ~307 | ~344 | ~>2000 (96.8%) | 560 | 67 | 3.73 | 0.135 | ||
| 652585 | PILKINGTON OPTICAL | LAC652585 | 1990 | H / I | 10MM | ----- | ~<360 (82.7%) | ~374 | ~>1000 (99.6%) | 550 | 69 | 3.81 | 0.138 | ||
| 652585 | SCHOTT GLASS TECH. | LaKN7 | 1992 | I | 5MM | ~<300 (14%) | ~322 | ~356 | ~>1970.1 (97.9%) | 460 | 716 | 71 | 3.84 | 0.139 | |
| 652585 | SCHOTT GLASS TECH. | NLAK7 | 2000 | P | 10MM | ~290 | ~333 | ~368 | ~>1970 (95.9%) | 600 | 71 | 3.84 | 0.139 | ||
| 653335 | PILKINGTON OPTICAL | EDF653335 | 1990 | H / I | 10MM | ------ | ~<360 (74.7%) | ~380 | ~>1000 (99.7%) | 380 | 84 | 3.90 | 0.141 | ||
| 654336 | OHARA CORP. | PBM29 | 1990 | H / I | 10MM | ~<330 (6%) | ~345 | ~374 | ~>1060 (99.9%) | 400 | 81 | 3.91 | 0.142 | ||
| 654337 | CHINA | ZF8 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 360 | 79 | 3.91 | 0.142 | ||
| 654337 | HOYA CORP. | FD9 | 1978 | H / I | 5MM | ~<330 (4%) | ~340 | ~365 | ~>700 (99.9%) | 430 | ----- | 3.88 | 0.140 | ||
| 654337 | SCHOTT GLASS TECH. | SF9 | 1992 | I | 5MM | ~320 | ~339 | ~362 | ~>2325.4 (94%) | 360 | 584 | 81 | 3.91 | 0.142 | |
| 654340 | HAYWARD SCIENTIFIC | DF8 | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ||
| 654396 | CHINA | TF5 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 515 | 48 | 3.58 | 0.130 | ||
| 654396 | HOYA CORP. | ADF50 | DERIVED | HYPOTHETICAL | 1MM* | ------ | ~<340 (81.5%) | ~348 | ~>700 (99.9%) | 435 | ---- | 3.48 | 0.126 | ||
| 654396 | HOYA CORP. | ADF50 | 1998 | P | 5MM | ~<330 (7%) | ~345 | ~369 | ~>700 (99.9%) | 435 | ----- | 3.48 | 0.126 | ||
| 654396 | HOYA CORP. | EADF50 | DERIVED | HYPOTHETICAL | 1MM* | ------ | ~<350 (78.6%) | ~359 | ~>1550 (99.7%) | 460 | ----- | 3.38 | 0.122 | ||
| 654396 | HOYA CORP. | EADF50 | 1998 | P/EG | 5MM | ~<340 (6%) | ~356 | ~383 | ~>1550 (98.6%) | 460 | ----- | 3.38 | 0.122 | ||
| 654396 | SCHOTT GLASS TECH. | KzFSN5 | 2000 | P | 10MM | ~<334 (13%) | ~350 | ~372 | ~>1530 (96.7%) | 460 | ----- | 45 | 3.46 | 0.125 | |
| 654397 | OHARA CORP. | BPH5 | 1996 | I | 10MM | ~<320 (3%) | ~347 | ~382 | ~>2000 (92.1%) | 440 | 46 | 3.49 | 0.126 | ||
| 654397 | OHARA CORP. | S-NBH5 | 1999 | EG | 10MM | ~<330 (12%) | ~341 | ~370 | ~>2200 (91.9%) | 580 | 66 | 3.02 | 0.109 | ||
| 654447 | HOYA CORP. | ATF4 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 320 | 117 | 3.76 | 0.136 | ||
| 655329 | SCHOTT GLASS TECH. | SF50 | 1992 | H / I | 5MM | ~<350 (46%) | ~352 | ~369 | ~>700 (99.9%) | 360 | 543 | 101 | 3.79 | 0.137 | |
| 655334 | EAST GERMANY | SF9 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~<340 (17.0%) | ~354 | ~386 | ~>1500 (99.5%) | ----- | 59 | 3.93 | 0.142 | ||
| 655401 | CORNING-FRANCE | C55-40 | 1991 | P | 10MM | ~<310 (6.7%) | ~346 | ~383 | ~>1800 (97.3%) | ----- | 550 | 55 | 3.57 | 0.129 | |
| 657366 | BAUSCH & LOMB | ----- | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | 4.01 | 0.145 | ||
| 657367 | SCHOTT GLASS TECH. | BaSF56 | 1992 | I | 5MM | ~<350 (30%) | ~356 | ~376 | ~>2325.4 ((95.6%) | 430 | ----- | 81 | 3.85 | 0.139 | |
| 657509 | BAUSCH & LOMB | ----- | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | 3.69 | 0.134 | ||
| 657511 | CHINA | ZBAF3 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 460 | 73 | 3.98 | 0.144 | ||
| 657511 | RUSSIA | C127 | PRE 1992 | H / I | ----- | ----- | ----- | ----- | ----- | ----- | 73 | 3.98 | 0.144 | ||
| 657512 | HAYWARD SCIENTIFIC | DBF2 | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ||
| 657572 | BAUSCH & LOMB | ----- | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | 3.74 | 0.135 | ||
| 658509 | CHINA | ZBAF50 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 555 | ------ | 3.27 | 0.118 | ||
| 658509 | EAST GERMANY | SSK5 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~<360 (6.1%) | ~383 | ~420 | ~>1500 (98.2%) | ----- | 79 | 3.77 | 0.137 | ||
| 658509 | HIKARI GLASS CO. | E-SSK5 | 2001 | EG/P | 10MM | ~<340(8%) | ~354 | ~379 | ~>2200(94.1%) | 521 | 679 | ----- | 3.82 | 0.138 | |
| 658509 | HOYA CORP. | BaCED5 | DERIVED | HYPOTHETICAL | 1MM* | ----- | ~<320 (63.1%) | ~341 | ~>1550 (99.9%) | 580 | 72 | 3.64 | 0.132 | ||
| 658509 | HOYA CORP. | BaCED5 | 1998 | P | 5MM | ~<320 (11%) | ~336 | ~362 | ~> 1550 (99.8%) | 580 | 72 | 3.64 | 0.132 | ||
| 658509 | OHARA CORP. | BSM25 | 1990 | H / I | 10MM | ~<330 (4%) | ~348 | ~374 | ~>700 (99.6%) | 590 | 66 | 3.49 | 0.126 | ||
| 658509 | OHARA CORP. | S-BSM25 | ---- | P/EG | 10MM | ~<330 (3%) | ~351 | ~379 | ~>2200 (94.7%) | 560 | 68 | 3.50 | 0.127 | ||
| 658509 | PILKINGTON OPTICAL | DBC658509 | 1990 | H / I | 10MM | ------ | ~<360 (74.1%) | ~377 | ~>1000 (99.5%) | 560 | 70 | 3.77 | 0.137 | ||
| 658509 | PILKINGTON OPTICAL | DBC658509A | 2002 | EG | 5MM | ----- | ~<340 (57.8%) | ~370 | ~>2200.0 (96.0%) | 569 | 80 | 3.56 | 0.129 | ||
| 658509 | SCHOTT GLASS TECH. | NSSK5 | 2000 | P | 10MM | ~<334 (2%) | ~356 | ~380 | ~1970 (96.3%) | 590 | 68 | 3.71 | 0.134 | ||
| 658509 | SCHOTT GLASS TECH. | SSK52 | 1992 | H / I | 5MM | ~<334.1 (24%) | ~344 | ~369 | ~>700 (99.8%) | 500 | ----- | 67 | 3.76 | 0.136 | |
| 658509 | SCHOTT GLASS TECH. | SSKN5 | 1992 | H / I | 5MM | ~<334.1 (9%) | ~346 | ~368 | ~>2325.4 (93%) | 470 | 751 | 68 | 3.71 | 0.134 | |
| 658534 | HOYA CORP. | LaCL30 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 555 | 84 | 3.80 | 0.138 | ||
| 658572 | CORNING-FRANCE | C57-57 | 1991 | P | 10MM | ~<290 (2%) | ~338 | ~371 | ~>1800 (98.3%) | ----- | 705 | 74 | 3.94 | 0.143 | |
| 658573 | HOYA CORP. | LaC11 | 1978 | H / I | 5MM | ~<300 (8%) | ~325 | ~360 | ~>700 (99.9%) | 615 | 68 | 3.63 | 0.131 | ||
| 658573 | OHARA CORP. | LAL11 | 1990 | I | 10MM | ~280 | ~320 | ~357 | ~>700 (99.8%) | 560 | 73 | 3.90 | 0.141 | ||
| 658573 | OHARA CORP. | S-LAL11 | 1996 | EG | ~280 | ~313 | ~351 | ~1800 | 560 | 73 | 3.90 | 0.141 | |||
| 658573 | PILKINGTON OPTICAL | LAC658573 | 1990 | H / I | 10MM | ------ | ~<360 (83.3%) | ~372 | ~>1000 (99.6%) | 580 | 73 | 3.78 | 0.137 | ||
| 658573 | SCHOTT GLASS TECH. | LaK11 | 1992 | I | 5MM | ~<290 (6%) | ~328 | ~364 | ~>2325.4 (91%) | 520 | 695 | 72 | 3.79 | 0.137 | |
| 659510 | CORNING-FRANCE | C58-51 | 1991 | P | 10MM | ~<310 (5) | ~334 | ~366 | ~>1800 (98.5%) | 526 | 705 | 64 | 3.27 | 0.118 | |
| 660329 | SCHOTT GLASS TECH. | SF51 | 1992 | H / I | 5MM | ~<350 (2%) | ~366 | ~386 | ~>700 (99.8%) | 380 | ----- | 78 | 3.81 | 0.138 | |
| 660574 | CHINA | LAK1 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 510 | 68 | 3.92 | 0.142 | ||
| 660574 | RUSSIA | C166 | PRE 1992 | H / I | ----- | ----- | ----- | ----- | ----- | ----- | 71 | 3.91 | 0.142 | ||
| 661415 | EAST GERMANY | BaSF9 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~<360 (15.7%) | ~375 | ~412 | ~>1500 (99.2%) | ----- | 73 | 3.79 | 0.137 | ||
| 663418 | RUSSIA | C391 | PRE 1992 | H / I | 10MM | ~<340 (27.6%) | ~353 | ~391 | ~>1500 (97.7%) | ----- | 46 | 3.60 | 0.130 | ||
| 664354 | RUSSIA | C248 | PRE 1992 | H / I | 10MM | ----- | ~<380 (80.0%) | ~400 | ~>1500 (99.2%) | ----- | 59 | 3.96 | 0.143 | ||
| 664355 | CHINA | ZBAF4 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 455 | 89 | 3.91 | 0.142 | ||
| 664358 | OHARA CORP. | BAH22 | 1990 | I | 10MM | ~<330 (2%) | ~348 | ~380 | ~>700 (99.8%) | 440 | 85 | 3.96 | 0.143 | ||
| 664358 | SCHOTT GLASS TECH. | BaSF2 | 1992 | I | 5MM | ~<350 (17%) | ~360 | ~382 | ~>2325.4 (95.9%) | 410 | 640 | 82 | 3.90 | 0.141 | |
| 664359 | EAST GERMANY | BaSF2 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~<360 (18.3%) | ~373 | ~400 | ~>1500 (99.1%) | ----- | 77 | 3.89 | 0.141 | ||
| 664359 | HIKARI GLASS CO. | E-BASF2 | 2001 | EG/P | 10MM | ~<360(5%) | ~375 | ~403 | ~>2400(90.6%) | 503 | 616 | ----- | 3.10 | 0.112 | |
| 664359 | HOYA CORP. | BaFD2 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 455 | ----- | 4.02 | 0.146 | ||
| 664489 | HOYA CORP. | BaF21 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 565 | 73 | 3.80 | 0.138 | ||
| 664564 | EAST GERMANY | SK24 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~<320 (2%) | ~352 | ~384 | ~>1500 (99.5%) | ----- | 77 | 4.00 | 0.145 | ||
| 665534 | HOYA CORP. | LaCL3 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 570 | ----- | 3.84 | 0.139 | ||
| 665546 | CHINA | LAK11 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | ----- | 4.01 | 0.145 | |||
| 667323 | HAYWARD SCIENTIFIC | EDF7 | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ||
| 667330 | OHARA CORP. | S-TIM39 | 1996 | P/EG | 10MM | ~<360 (3%) | ~375 | ~399 | ~>2200 (93.7%) | 550 | 87 | 2.92 | 0.106 | ||
| 667330 | SCHOTT GLASS TECH. | SF19 | 1992 | I | 5MM | ~<334.1 (27%) | ~341 | ~361 | ~>2325.4 (95.0%) | 360 | 593 | 77 | 4.02 | 0.146 | |
| 667331 | CORNING-FRANCE | C67-33 | 1991 | P | 10MM | ~<330 (5.5%) | ~347 | ~377 | ~>1800 (97.0%) | ----- | 593 | 76 | 3.98 | 0.144 | |
| 667331 | EAST GERMANY | SF19 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~<340 (6.0%) | ~360 | ~396 | ~>1500 (99.3%) | ----- | 61 | 4.02 | 0.146 | ||
| 667331 | HOYA CORP. | FD19 | 1978 | H / I | 5MM | ~<340 (38%) | ~345 | ~370 | ~>700 (99.9%) | 425 | ----- | 4.01 | 0.145 | ||
| 667331 | OHARA CORP. | PBM39 | 1990 | I | 10MM | ~330 | ~349 | ~380 | ~>1060 (99.9%) | 400 | 76 | 4.02 | 0.146 | ||
| 667482 | SCHOTT GLASS TECH. | BaF54 | 1992 | H / I | 5MM | ~<334.1 (9%) | ~352 | ~377 | ~>700 (99.8%) | 530 | ----- | 62 | 3.78 | 0.137 | |
| 667483 | HIKARI GLASS CO. | E-BAF11 | 2001 | EG/P | 10MM | ---- | ---- | ---- | ---- | 546 | 701 | ----- | 3.53 | 0.128 | |
| 667483 | HOYA CORP. | BaF11 | DERIVED | HYPOTHETICAL | 1MM* | ---- | ~<330 (63.1%) | ~353 | ~>1550 (99.9%) | 610 | 71 | 3.63 | 0.131 | ||
| 667483 | HOYA CORP. | BaF11 | 1998 | P | 5MM | ~<330 (8%) | ~349 | ~369 | ~>1550 (99.9%) | 610 | 71 | 3.63 | 0.131 | ||
| 667483 | OHARA CORP. | S-BAH11 | 1996 | P/EG | 10MM | ~<340 (4%) | ~358 | ~386 | ~>2200 (93.6%) | 560 | 69 | 3.59 | 0.130 | ||
| 667484 | CHINA | ZBAF16 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 470 | 71 | 3.76 | 0.136 | ||
| 667484 | CORNING-FRANCE | C67-48 | 1991 | P | 10MM | ~<330 (10.0%) | ~354 | ~379 | ~>1800 (98.2%) | ----- | 769 | 70 | 4.03 | 0.146 | |
| 667484 | SCHOTT GLASS TECH. | BaFN11 | 1992 | I | 5MM | ~<334.1 (2%) | ~352 | ~375 | ~>2325.4 (93%) | 470 | 750 | 68 | 3.76 | 0.136 | |
| 668323 | BAUSCH & LOMB | ----- | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | 4.03 | 0.146 | ||
| 668419 | CHINA | ZBAF17 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 445 | 72 | 3.76 | 0.136 | ||
| 668419 | EAST GERMANY | BaSF6 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~<360 (7%) | ~482 | ~423 | ~>1500 (98.9%) | ----- | 74 | 3.79 | 0.137 | ||
| 668419 | HOYA CORP. | BaFD6 | 1978 | H / I | 5MM | ~<350 (14%) | ~365 | ~390 | ~>700 (99.9%) | 530 | 75 | 3.79 | 0.137 | ||
| 668419 | OHARA CORP. | BAH26 | 1990 | I | 10MM | ~<350 (3%) | ~368 | ~396 | ~>1060 (99.7%) | 500 | 75 | 3.80 | 0.138 | ||
| 668419 | SCHOTT GLASS TECH. | BaSF6 | 1992 | I | 5MM | ~<350 (26%) | ~358 | ~388 | ~>2325.4 (95.2%) | 450 | 706 | 74 | 3.79 | 0.137 | |
| 668420 | HIKARI GLASS CO. | E-BASF6 | 2001 | EG/P | 10MM | ---- | ---- | ---- | ---- | 510 | 642 | ----- | 3.20 | 0.116 | |
| 669449 | HOYA CORP. | BaF13 | 1978 | H / I | 5MM | ~<340 (9%) | ~348 | ~390 | ~>700 (99.9%) | 545 | ----- | 3.88 | 0.140 | ||
| 669450 | OHARA CORP. | BAH13 | 1990 | I | 10MM | ~350 | ~365 | ~391 | ~>1060 (99.6%) | 500 | 76 | 4.00 | 0.145 | ||
| 669450 | SCHOTT GLASS TECH. | BaF13 | 1992 | I | 5MM | ~<350 (21%) | ~359 | ~382 | ~>2325.4 (94%) | 470 | 719 | 74 | 3.80 | 0.138 | |
| 669574 | PILKINGTON OPTICAL | LAC669574 | 1990 | H / I | 10MM | ----- | ~<360 (82.0%) | ~374 | ~>1000 (99.5%) | 580 | 72 | 3.94 | 0.143 | ||
| 669574 | SCHOTT GLASS TECH. | LaK23 | 1992 | I | 5MM | ~<290 (10%) | ~320 | ~359 | ~>2325.4 (92%) | 460 | 696 | 79 | 4.00 | 0.145 | |
| 670392 | CHINA | ZBAF18 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 430 | 77 | 3.90 | 0.141 | ||
| 670392 | SCHOTT GLASS TECH. | BaSF12 | 1992 | I | 5MM | ~<350 (24%) | ~358 | ~380 | ~>2325.4 (94%) | 430 | 656 | 79 | 3.90 | 0.141 | |
| 670393 | OHARA CORP. | BAH32 | 1996 | H / I | 10MM | ~<330 (4%) | ~346 | ~372 | ~>2400 (92.7%) | 480 | 70 | 4.02 | 0.146 | ||
| 670393 | OHARA CORP. | S-BAH32 | 1999 | P/EG | 10MM | ~<360 (16%) | ~370 | ~400 | ~>2200 (94.8%) | 580 | 69 | 3.26 | 0.118 | ||
| 670471 | CORNING-FRANCE | C70-47 | 1991 | P | 10MM | ~<320 (6.9%) | ~341 | ~370 | ~>1800 (98.2%) | 504 | 720 | 64 | 3.62 | 0.131 | |
| 670471 | SCHOTT GLASS TECH. | BAF53 | 1992 | H / I | 5MM | ~334.1 | ~354 | ~379 | ~>700 (99.9%) | 510 | ----- | 65 | 3.75 | 0.136 | |
| 670471 | SCHOTT GLASS TECH. | BaFN10 | 1992 | I | 5MM | ~<350 (34%) | ~356 | ~379 | ~>2325.4 (93%) | 480 | 745 | 68 | 3.76 | 0.136 | |
| 670471 | SCHOTT GLASS TECH. | BaFN10 | 1992 | H / I | 5MM | ~<350 (34%) | ~356 | ~379 | ~>2325.4 (93%) | 480 | 68 | 3.76 | 0.136 | ||
| 670471 | SCHOTT GLASS TECH. | NBAF10 | 2000 | P/EG | 10MM | ~<350 (18%) | ~361 | ~387 | ~>1970 (96.7%) | 620 | ----- | 62 | 3.75 | 0.136 | |
| 670472 | BAUSCH & LOMB | ----- | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | 3.78 | 0.137 | ||
| 670472 | EAST GERMANY | BaF10 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~<360 (12.6%) | ~376 | ~417 | ~>1500 (99.3%) | ----- | 71 | 3.80 | 0.138 | ||
| 670472 | HIKARI GLASS CO. | E-BAF10 | 2001 | EG/P | 10MM | ~<340(3%) | ~357 | ~380 | ~>2200 (98.5%) | 503 | 663 | ----- | 3.82 | 0.138 | |
| 670472 | HOYA CORP. | BaF10 | DERIVED | HYPOTHETICAL | 1MM* | ----- | ~<340 (74.1%) | ~351 | ~>700 (99.9%) | 610 | 72 | 3.61 | 0.131 | ||
| 670472 | HOYA CORP. | BaF10 | 1998 | P | 5MM | ~<340 (22%) | ~348 | ~372 | ~700 (99.9%) | 610 | 72 | 3.61 | 0.131 | ||
| 670473 | OHARA CORP. | BAH10 | 1990 | H / I | 10MM | ~<350 (5%) | ~368 | ~396 | ~>1060 (99.8%) | 540 | 71 | 3.77 | 0.137 | ||
| 670473 | OHARA CORP. | S-BAH10 | 1996 | P/EG | 10MM | ~340 | ~361 | ~390 | ~>2200 (94.9%) | 560 | 68 | 3.48 | 0.126 | ||
| 670474 | HAYWARD SCIENTIFIC | DBF3 | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ||
| 670516 | OHARA CORP. | LAL53 | 1990 | H / I | 10MM | ~<340 (13%) | ~352 | ~378 | ~>700 (99.6%) | 500 | 76 | 3.90 | 0.141 | ||
| 670517 | HOYA CORP. | LaCL4 | 1978 | H / I | 5MM | ~<340 (34%) | ~345 | ~380 | ~>700 (99.9%) | 550 | 70 | 3.90 | 0.141 | ||
| 670573 | HIKARI GLASS CO. | E-LAK02 | 2001 | EG/P | 10MM | ~<290(4%) | ~318 | ~357 | ~>2000(96.6%) | 631 | 672 | ----- | 3.74 | 0.135 | |
| 670573 | HOYA CORP. | LaCL7 | 1978 | H / I | 5MM | ~<290 (4%) | ~325 | ~360 | ~>700 (99.9%) | 615 | ---- | 3.56 | 0.129 | ||
| 670573 | OHARA CORP. | LAL52 | 1990 | H / I | 10MM | ~<280 (2%) | ~321 | ~359 | ~>700 (99.8%) | 540 | 74 | 3.96 | 0.143 | ||
| 670573 | OHARA CORP. | S-LAL52 | ---- | P/EG | ---- | ----- | ---- | ---- | ---- | 540 | 74 | 3.96 | 0.143 | ||
| 671473 | CHINA | ZBAF5 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 610 | 70 | 3.61 | 0.131 | ||
| 671493 | RUSSIA | C233 | PRE 1992 | H / I | 10MM | ~<340 (4.7%) | ~360 | ~396 | ~>1500 (99.3%) | ----- | 78 | 4.02 | 0.146 | ||
| 671520 | HAYWARD SCIENTIFIC | DBF6 | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ||
| 673289 | SCHOTT GLASS TECH. | TiSF1 | 1992 | H / I | 5MM | ~350 | ~367 | ~388 | ~>700 (99.9%) | 450 | ----- | 90 | 2.81 | 0.102 | |
| 673321 | HIKARI GLASS CO. | E-SF5 | 2001 | EG/P | 10MM | ~<360(1%) | ~379 | ~403 | ~>700(99.9%) | 612 | 621 | ----- | 2.89 | 0.105 | |
| 673321 | PILKINGTON OPTICAL | LDF673321A | 2003 | EG | 5MM | ----- | ~<380 (78.5%) | ~390 (90.2%) | ~>2200 (94.5%) | 566 | 77 | 2.90 | 0.105 | ||
| 673321 | OHARA CORP. | PBM25 | 1990 | I | 10MM | ~330 | ~348 | ~379 | ~>1060 (99.9%) | 390 | 85 | 4.07 | 0.147 | ||
| 673321 | OHARA CORP. | S-TIM25 | 1996 | P/EG | 10MM | ~360 | ~377 | ~403 | ~>2200 (94.4%) | 570 | 79 | 2.91 | 0.105 | ||
| 673322 | BAUSCH & LOMB | ----- | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | 3.97 | 0.144 | ||
| 673322 | CHINA | ZF2 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 410 | 77 | 4.08 | 0.148 | ||
| 673322 | EAST GERMANY | SF5 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~<340 (6.5%) | ~362 | ~399 | ~>1500 (99.4%) | ----- | 84 | 4.09 | 0.148 | ||
| 673322 | HAYWARD SCIENTIFIC | EDF2 | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ||
| 673322 | HIKARI GLASS CO. | SF5 | 2001 | I | 10MM | ~<340(15%) | ~349 | ~369 | ~>2400 (95.1%) | 373 | 480 | ----- | 4.09 | 0.148 | |
| 673322 | HOYA CORP. | EFD5 | DERIVED | HYPOTHETICAL | 1MM* | ----- | ~<360 (74.1%) | ~370 | ~>1550 (99.9%) | 520 | 89 | 2.90 | 0.105 | ||
| 673322 | HOYA CORP. | EFD5 | 1998 | P | 5MM | ~<350 (3%) | ~368 | ~388 | ~>1550 (99.7%) | 520 | 89 | 2.90 | 0.105 | ||
| 673322 | HOYA CORP. | FD5 | DERIVED | HYPOTHETICAL | 1MM* | ----- | ~<340 (82.2%) | ~347 | ~>1550 (99.9%) | 410 | 79 | 4.08 | 0.148 | ||
| 673322 | HOYA CORP. | FD5 | 1998 | P | 5MM | ~<330 (6%) | ~343 | ~362 | ~>1550 (99.7%) | 410 | 79 | 4.08 | 0.148 | ||
| 673322 | PILKINGTON OPTICAL | EDF673322 | 1990 | H / I | 10MM | ----- | ----- | ----- | ----- | 370 | 85 | 4.07 | 0.147 | ||
| 673322 | PILKINGTON OPTICAL | EDF673322A | 2002 | EG | 5MM | ----- | ~<340 (66.7%) | ~359 | ~>2200.0 (94.6%) | 378 | 87 | 4.07 | 0.147 | ||
| 673322 | RUSSIA | C343 | PRE 1992 | H / I | 10MM | ~<340 (1.5%) | ~366 | ~400 | ~>1500 (99.3%) | ----- | 73 | 4.09 | 0.148 | ||
| 673322 | SCHOTT GLASS TECH. | SF5 | 2000 | P | 10MM | ~<334 (20%) | ~345 | ~368 | ~>1970 (95.9%) | 410 | ----- | 82 | 4.07 | 0.147 | |
| 673323 | CORNING-FRANCE | C72-32 | 1991 | P | 10MM | ~320 | ~348 | ~380 | ~>1800 (97.4%) | ---- | 562 | 74 | 4.06 | 0.147 | |
| 673323 | SCHOTT GLASS TECH. | NSF5 | 2000 | P/EG | 10MM | ~<365 (12%) | ~376 | ~399 | ~>1970 (95.0%) | 620 | 79 | 2.86 | 0.104 | ||
| 677375 | HOYA CORP. | ADF405 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 465 | 65 | 3.79 | 0.137 | ||
| 677375 | OHARA CORP. | BPH40 | 1990 | I | 10MM | ~<330 (2%) | ~361 | ~396 | ~>700 (99.8%) | 460 | 53 | 3.76 | 0.136 | ||
| 678338 | HOYA CORP. | EFD2 | 1998 | P/EG | 5MM | ~<350 (3%) | ~366 | ~386 | ~>1550 (99.8%) | 525 | 88 | 2.77 | 0.100 | ||
| 678506 | HOYA CORP. | LaCL9 | DERIVED | HYPOTHETICAL | 1MM* | ------ | ~<330 (70.4%) | ~344 | ~>1550 (99.9%) | 600 | ----- | 3.90 | 0.141 | ||
| 678506 | HOYA CORP. | LaCL9 | 1998 | P | 5MM | ~<330 (16%) | ~340 | ~365 | ~>1550 (99.7%) | 600 | 3.90 | 0.141 | |||
| 678507 | HIKARI GLASS CO. | E-LAK06 | 2001 | EG/P | 10MM | ---- | ---- | ---- | ---- | 485 | 671 | ----- | 3.86 | 0.140 | |
| 678507 | OHARA CORP. | LAL56 | 1990 | H / I | 10MM | ~<340 (9%) | ~355 | ~384 | ~>700 (99.6%) | 550 | 76 | 3.96 | 0.143 | ||
| 678507 | OHARA CORP. | S-LAL56 | 1996 | P/EG | 10MM | ~330 | ~350 | ~376 | ~>2200 (92.8%) | 540 | 66 | 3.85 | 0.139 | ||
| 678534 | HOYA CORP. | LaCL8 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 555 | ----- | 3.81 | 0.138 | ||
| 678534 | OHARA CORP. | LAL57 | 1990 | H / I | 10MM | ~<330 (6%) | ~348 | ~376 | ~>700 (99.6%) | 500 | 77 | 4.03 | 0.146 | ||
| 678549 | OHARA CORP. | L-LAL12 | 1999 | 10MM | ~290 | ~334 | ~366 | ~>900 (99.8%) | 610 | 76 | 3.52 | 0.127 | |||
| 678549 | SCHOTT GLASS TECH. | LAKL12 | 2000 | P | 10MM | ~300 | ~330 | ~365 | ~>1970 (96.3%) | 700 | ----- | 68 | 3.32 | 0.120 | |
| 678550 | EAST GERMANY | SK22 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~320 | ~356 | ~391 | ~>1500 (99.0%) | ----- | 66 | 4.03 | 0.146 | ||
| 678552 | PILKINGTON OPTICAL | LAC678552B | 1990 | I | 5MM | ----- | ~<360 (80.8%) | ~373 | ~>1000 (99.4%) | 550 | 79 | 4.06 | 0.147 | ||
| 678552 | SCHOTT GLASS TECH. | LaKN12 | 1992 | H / I | 5MM | ~<300 (3%) | ~334.1 | ~365.0 | ~>1970.1 (97.3%) | 470 | 714 | 76 | 4.10 | 0.148 | |
| 678552 | SCHOTT GLASS TECH. | NLAK12 | 2000 | P | 10MM | ~<310 (3%) | ~336 | ~368 | ~>1970 (94.0%) | 560 | 76 | 4.10 | 0.148 | ||
| 678553 | OHARA CORP. | LAL12 | 1990 | H / I | 10MM | ~<290 (5%) | ~320 | ~357 | ~>700 (99.8%) | 500 | 72 | 4.01 | 0.145 | ||
| 678553 | OHARA CORP. | S-LAL12 | 1996 | P/EG | 10MM | ~<280 (6%) | ~313 | ~352 | ~>2000 (96.3%) | 560 | 72 | 4.01 | 0.145 | ||
| 678554 | HIKARI GLASS CO. | E-LAK12 | 2001 | EG/P | 10MM | ~<290(1%) | ~319 | ~354 | ~>2000(96%) | 530 | 677 | ----- | 3.96 | 0.143 | |
| 678555 | CHINA | LAK5 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 470 | 77 | 4.08 | 0.148 | ||
| 678555 | CORNING-FRANCE | C78-56 | 1991 | P | 10MM | ~<280 (9%) | ~327 | ~365 | ~>1800 (97.7%) | ----- | 723 | 67 | 3.59 | 0.130 | |
| 678555 | HOYA CORP. | LaC12 | DERIVED | HYPOTHETICAL | 1MM* | ----- | ~<300 (63.1%) | ~337 | ~>1550 (99.9%) | 590 | 77 | 3.80 | 0.138 | ||
| 678555 | HOYA CORP. | LaC12 | 1998 | P | 5MM | ~<290 (4%) | ~331 | ~365 | ~>1550 (99.6%) | 590 | 77 | 3.80 | 0.138 | ||
| 681319 | SCHOTT GLASS TECH. | SF62 | 1992 | H / I | 5MM | ~320 | ~342 | ~362 | ~>700 (99.9%) | 360 | 581 | 82 | 4.15 | 0.150 | |
| 681372 | CHINA | TF6 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 450 | 48 | 3.84 | 0.139 | ||
| 681372 | SCHOTT GLASS TECH. | KzFSN7 | 1992 | H / I | 5MM | ~<350 (7%) | ~362 | ~370 | ~>700 (99.9%) | 450 | 48 | 3.51 | 0.127 | ||
| 681732 | SCHOTT GLASS TECH. | KzFS7A | 1992 | I | 5MM | ~<334.1 (10%) | ~352 | ~373 | ~>1970.1 (95.7%) | 450 | ----- | 49 | 3.73 | 0.135 | |
| 682482 | CHINA | ----- | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | ----- | 3.87 | 0.140 | |||
| 682482 | HOYA CORP. | LaFL20 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 585 | 97 | 3.82 | 0.138 | ||
| 682482 | SCHOTT GLASS TECH. | LaF20 | 1992 | I | 5MM | ~<334.1 (8%) | ~347 | ~373 | ~>2325.4 (96.6%) | 520 | 743 | 74 | 3.87 | 0.140 | |
| 683445 | CHINA | ZBAF51 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 590 | ------ | 3.80 | 0.138 | ||
| 683445 | SCHOTT GLASS TECH. | BaF50 | 1992 | I | 5MM | ~<334.1 (6%) | ~354 | ~380 | ~>2325.4 (91%) | 490 | 682 | 83 | 3.80 | 0.138 | |
| 683447 | HOYA CORP. | BaF22 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 550 | ----- | 3.88 | 0.140 | ||
| 683447 | OHARA CORP. | BAH51 | 1990 | H / I | 10MM | ~<360 (9%) | ~377 | ~409 | ~>1060 (99.7%) | 540 | 74 | 3.96 | 0.143 | ||
| 686439 | HOYA CORP. | BaF20 | 1978 | H / I | 5MM | ~<350 (9%) | ~363 | ~390 | ~>700 (99.9%) | 540 | ----- | 3.88 | 0.140 | ||
| 686440 | OHARA CORP. | BAH53 | 1990 | H / I | 10MM | ~<360 (9%) | ~376 | ~407 | ~>1060 (99.7%) | 480 | 72 | 3.96 | 0.143 | ||
| 686492 | OHARA CORP. | LAM56 | 1990 | H / I | 10MM | ~<340 (5%) | ~357 | ~387 | ~>1060 (99.5%) | 520 | 77 | 3.99 | 0.144 | ||
| 686494 | HOYA CORP. | LaFL1 | 1978 | H / I | 5MM | ~<340 (13%) | ~355 | ~380 | ~>700 (99.9%) | 515 | ----- | 4.11 | 0.149 | ||
| 687429 | HOYA CORP. | ADF8 | 1978 | H / I | 5MM | ~<330 (16%) | ~355 | ~390 | ~>700 (99.8%) | 575 | 53 | 3.70 | 0.134 | ||
| 687536 | RUSSIA | C168 | PRE 1992 | H / I | ----- | ----- | ----- | ----- | ----- | ----- | 84 | 4.33 | 0.157 | ||
| 689306 | SCHOTT GLASS TECH. | SF52 | 1992 | H / I | 5MM | ~<350 (18%) | ~358 | ~375 | ~>700 (99.9%) | 350 | 547 | 95 | 4.10 | 0.148 | |
| 689309 | BAUSCH & LOMB | ----- | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | 4.24 | 0.154 | ||
| 689309 | HAYWARD SCIENTIFIC | EDF4 | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ----- | ||
| 689311 | HIKARI GLASS CO. | E-SF8 | 2001 | EG/P | 10MM | ~<360(1%) | ~378 | ~399 | ~>2200(91.1%) | 566 | 622 | ----- | 2.93 | 0.106 | |
| 689311 | OHARA CORP. | L-TIM28 | 1999 | 10MM | ~<360 (16%) | ~368 | ~393 | ~>600 (99.6%) | 530 | 101 | 2.88 | 0.104 | |||
| 689311 | OHARA CORP. | PBM28 | 1990 | I | 10MM | ~<340 (16%) | ~350 | ~386 | ~>1060 (99.9%) | 370 | 86 | 4.22 | 0.153 | ||
| 689311 | OHARA CORP. | PBM28W | ------ | I | ------ | ------ | ------ | -------- | ------ | ------ | ----- | ----- | ----- | ||
| 689311 | OHARA CORP. | S-TIM28 | 1996 | P/EG | 10MM | ~360 | ~378 | ~406 | ~>2200 (96.1%) | 550 | 82 | 2.98 | 0.108 | ||
| 689311 | RUSSIA | C353 | PRE 1992 | H / I | 10MM | ----- | ~380 (84.1%) | ~396 | ~>1500 (99.3%) | ----- | 76 | 4.23 | 0.153 | ||
| 689312 | CHINA | ZF10 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 335 | 79 | 4.22 | 0.153 | ||
| 689312 | CORNING-FRANCE | C89-31 | 1991 | P | 10MM | ~<330 (11.5%) | ~354 | ~390 | ~>1800 (97.4%) | ---- | 553 | 77 | 4.22 | 0.153 | |
| 689312 | EAST GERMANY | SF8 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~340 | ~368 | ~405 | ~>1500 (99.8%) | ----- | 83 | 4.23 | 0.153 | ||
| 689312 | HIKARI GLASS CO. | SF8 | 2001 | I | 10MM | ~<340(11%) | ~350 | ~369 | ~>2400 (96.2%) | 987 | 470 | ----- | 4.22 | 0.153 | |
| 689312 | HOYA CORP. | EFD8 | DERIVED | HYPOTHETICAL | 1MM* | ---- | ~<360 (72.5%) | ~372 | ~>1550 (99.9%) | 530 | 93 | 2.97 | 0.108 | ||
| 689312 | HOYA CORP. | EFD8 | 1998 | P/EG | 5MM | ~<350 (2%) | ~369 | ~392 | ~>1550 (99.8%) | 530 | 93 | 2.97 | 0.108 | ||
| 689312 | HOYA CORP. | FD8 | DERIVED | HYPOTHETICAL | 1MM* | ---- | ~<340 (72.5%) | ~350 | ~>1550 (99.9%) | 400 | 77 | 4.21 | 0.152 | ||
| 689312 | HOYA CORP. | FD8 | 1998 | P | 5MM | ~<340 (19%) | ~348 | ~368 | ~>1550 (99.8%) | 400 | 77 | 4.21 | 0.152 | ||
| 689312 | PILKINGTON OPTICAL | EDF689312 | 1990 | H / I | 10MM | ----- | ----- | ----- | ----- | 380 | 75 | 4.24 | 0.154 | ||
| 689312 | PILKINGTON OPTICAL | EDF689312A | 2002 | EG | 5MM | ----- | ~<350 (65.2%) | ~368 | ~>2200.0 (96.7%) | 386 | 74 | 4.24 | 0.154 | ||
| 689312 | SCHOTT GLASS TECH. | SF8 | 1992 | I | 5MM | ~<334.1 (14%) | ~344 | ~365.0 | ~>2325.4 (94%) | 340 | 576 | 82 | 4.22 | 0.153 | |
| 689313 | SCHOTT GLASS TECH. | NSF8 | 2000 | P/EG | 10MM | ~<365 (16%) | ~375 | ~400 | ~>1970 (95.0%) | 600 | 86 | 2.90 | 0.105 | ||
| 689495 | HOYA CORP. | LaFL23 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 595 | 86 | 4.01 | 0.145 | ||
| 689495 | PILKINGTON OPTICAL | LAFA689495 | 1990 | H / I | 10MM | ----- | ~<360 (83.7%) | ~372 | ~>1000 (99.2%) | ----- | 75 | 3.70 | 0.134 | ||
| 689496 | CORNING-FRANCE | C90-50 | 1991 | P | 10MM | ~280 | ~348 | ~370 | ~>1800 (98.3%) | ---- | 742 | 72 | 3.66 | 0.133 | |
| 689497 | PILKINGTON OPTICAL | LAF689497B | 2002 | I | 5MM | ----- | ----- | ----- | ----- | 560 | 75 | 3.70 | 0.134 | ||
| 689497 | SCHOTT GLASS TECH. | LaFN23 | 1992 | I | 5MM | ~<334.1 (27%) | ~342 | ~364 | ~>1970.1 (97.9%) | 400 | 704 | 81 | 4.20 | 0.152 | |
| 691547 | HOYA CORP. | LaC9 | DERIVED | HYPOTHETICAL | 1MM* | ----- | ~<280 (70.4%) | ~318 | ~>1550 (99.9%) | 695 | 58 | 3.65 | 0.132 | ||
| 691547 | HOYA CORP. | LaC9 | 1998 | P | 5MM | ~<280 (10%) | ~315 | ~352 | ~>1550 (99.7%) | 695 | 58 | 3.65 | 0.132 | ||
| 691547 | PILKINGTON OPTICAL | LACA691547B | 2002 | I | 5MM | ----- | ~<360 (88.3%) | ~364 | ~>1000 (99.6%) | 640 | 72 | 3.52 | 0.127 | ||
| 691547 | SCHOTT GLASS TECH. | LaK9 | 1992 | H / I | 5MM | ~<280 (5%) | ~317 | ~352 | ~>1970.1 (98.6%) | 580 | 722 | 63 | 3.51 | 0.127 | |
| 691547 | SCHOTT GLASS TECH. | NLAK9 | 2000 | P | 10MM | ~290 | ~331 | ~364 | ~>1970 (95.9%) | 700 | 63 | 3.51 | 0.127 | ||
| 691548 | BAUSCH & LOMB | ----- | PRE-1979 | NA | ----- | ----- | ----- | ----- | ----- | ----- | ----- | 4.03 | 0.146 | ||
| 691548 | CORNING-FRANCE | C90-55 | 1991 | P | 10MM | ~<290 (2%) | ~343 | ~376 | ~>1800 (98.3%) | 532 | 701 | 72 | 3.67 | 0.133 | |
| 691548 | HIKARI GLASS CO. | E-LAK9 | 2001 | EG/P | 10MM | ---- | ---- | ---- | ---- | 679 | 683 | ----- | 3.48 | 0.126 | |
| 691548 | OHARA CORP. | LAL9 | 1990 | H / I | 10MM | ~<300 (3%) | ~337 | ~374 | ~>700 (99.6%) | 670 | 62 | 3.63 | 0.131 | ||
| 691548 | OHARA CORP. | S-LAL9 | 1996 | P/EG | 10MM | ~290 | ~337 | ~372 | ~>2000 (96.3%) | 660 | 61 | 3.63 | 0.131 | ||
| 691548 | PILKINGTON OPTICAL | LACB691548 | 1990 | H / I | 10MM | ----- | ~<360 (79.6%) | ~376 | ~>1000 (99.4%) | 540 | 82 | 4.18 | 0.151 | ||
| 692545 | CHINA | LAK2 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 555 | 60 | 3.68 | 0.133 | ||
| 692550 | RUSSIA | C174 | PRE 1992 | H / I | 10MM | ~<300 (6.3%) | ~336 | ~379 | ~>1500 (99.4%) | ----- | 57 | 3.46 | 0.125 | ||
| 693516 | SCHOTT GLASS TECH. | Lak20 | 1992 | H / I | 5MM | ~<320 (5%) | ~347 | ~376 | ~>700 (99.9%) | 440 | ----- | 82 | 4.13 | 0.150 | |
| 693536 | EAST GERMANY | SSK10 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~<340 (8.2%) | ~362 | ~398 | ~>1500 (99.2%) | ----- | 68 | 4.38 | 0.159 | ||
| 694492 | CHINA | LAF1 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | ----- | 91 | 4.41 | 0.160 | ||
| 694508 | HOYA CORP. | LaCL5 | DERIVED | HYPOTHETICAL | 1MM* | ----- | ~<320 (63.1%) | ~338 | ~>1550 (99.9%) | 565 | 78 | 4.15 | 0.150 | ||
| 694508 | HOYA CORP. | LaCL5 | 1998 | P | 5MM | ~<320 (10%) | ~335 | ~358 | ~>1550 (99.7%) | 565 | 78 | 4.15 | 0.150 | ||
| 694508 | OHARA CORP. | LAL58 | 1996 | H / I | 10MM | ~<330 (2%) | ~348 | ~375 | ~>2200 (93.0%) | 510 | 78 | 4.11 | 0.149 | ||
| 694508 | OHARA CORP. | S-LAL58 | 1999 | P/EG | 10MM | ~<320 (2%) | ~339 | ~365 | ~>2200 (94.2%) | 580 | 75 | 4.03 | 0.146 | ||
| 694532 | HIKARI GLASS CO. | E-LAK13 | 2001 | EG/P | 10MM | ~<290(1%) | ~323 | ~358 | ~>2200(91.6%) | 618 | 650 | ----- | 3.68 | 0.133 | |
| 694532 | HOYA CORP. | MLaC130 | DERIVED | HYPOTHETICAL | 1MM* | ---- | ~<290 (72.5%) | ~315 | ~>700 (99.9%) | 650 | 69 | 3.52 | 0.127 | ||
| 694532 | HOYA CORP. | MLaC130 | 1998 | P | 5MM | ~<280 (6%) | ~309 | ~347 | ~>700 (99.9%) | 650 | 69 | 3.52 | 0.127 | ||
| 694532 | OHARA CORP. | LAL13 | 1990 | H / I | 10MM | ~<300 (2%) | ~341 | ~374 | ~>700 (99.7%) | 660 | 60 | 3.60 | 0.130 | ||
| 694532 | OHARA CORP. | S-LAL13 | 1996 | P/EG | 10MM | ~290 | ~339 | ~374 | ~>2000 (95.8%) | 650 | 57 | 3.60 | 0.130 | ||
| 694533 | HOYA CORP. | LaC13 | DERIVED | HYPOTHETICAL | 1MM* | ----- | ~<300 (70.4%) | ~321 | ~>1550 (99.9%) | 700 | 53 | 3.56 | 0.129 | ||
| 694533 | HOYA CORP. | LaC13 | 1998 | P | 5MM | ~<290 (6%) | ~315 | ~350 | ~>1550 (99.4%) | 700 | 53 | 3.56 | 0.129 | ||
| 694533 | PILKINGTON OPTICAL | LAC694533 | 1990 | H / I | 10MM | ----- | ~<360 (69.4%) | ~381 | ~>1000 (99.4%) | 530 | 80 | 4.18 | 0.151 | ||
| 694533 | SCHOTT GLASS TECH. | LAKN13 | 2000 | H / I | 10MM | ~<310 (7%) | ~330 | ~364 | ~>1970 (96.3%) | 560 | 84 | 4.24 | 0.154 | ||
| 694533 | SCHOTT GLASS TECH. | LaKN13 | 1992 | H / I | 5MM | ~<300 (7%) | ~327 | ~362 | ~>1970.1 (98.3%) | 470 | 718 | 84 | 4.24 | 0.154 | |
| 694534 | CHINA | LAK6 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 485 | 82 | 4.29 | 0.155 | ||
| 695422 | OHARA CORP. | BAH54 | 1990 | H / I | 10MM | ~<330 (9%) | ~346 | ~376 | ~>700 (99.8%) | 610 | 66 | 2.51 | 0.091 | ||
| 695422 | OHARA CORP. | S-BAH54 | ---- | EG | ---- | ----- | ------- | ----- | ----- | 610 | 66 | 3.30 | 0.119 | ||
| 696365 | CORNING-FRANCE | C97-36 | 1991 | P | 10MM | ~<320 (5%) | ~356 | ~394 | ~>1800 (98.0%) | ----- | 537 | 40 | 3.93 | 0.142 | |
| 697470 | EAST GERMANY | D401 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ----- | ----- | ~<440 (96.0%) | ~>540 (99.8%) | ----- | 79 | 4.08 | 0.148 | ||
| 697485 | HIKARI GLASS CO. | E-LAF09 | 2001 | EG/P | 10MM | ---- | ---- | ---- | ---- | 602 | 698 | ----- | 3.67 | 0.133 | |
| 697485 | HOYA CORP. | LaFL2 | DERIVED | HYPOTHETICAL | 1MM* | ----- | ~>1550 (99.9%) | 585 | ----- | 4.05 | 0.147 | ||||
| 697485 | HOYA CORP. | LaFL2 | 1998 | P | 5MM | ~<330 (17%) | ~340 | ~365 | ~>1550 (99.7%) | 585 | ----- | 4.05 | 0.147 | ||
| 697485 | OHARA CORP. | LAM59 | 1996 | H / I | 10MM | ~<340 (4%) | ~357 | ~384 | ~>2200 (92.1%) | 530 | 75 | 4.06 | 0.147 | ||
| 697485 | OHARA CORP. | S-LAM59 | 1999 | P/EG | 10MM | ~<340 (14%) | ~351 | ~376 | ~>2200 (95.2%) | 600 | 71 | 3.77 | 0.137 | ||
| 697554 | CHINA | ----- | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | ----- | 3.63 | 0.131 | |||
| 697554 | CORNING-FRANCE | C97-55 | 1991 | P | 10MM | ~<280 (3.3%) | ~329 | ~368 | ~>1800 (98.2%) | ----- | ----- | 53 | 3.62 | 0.131 | |
| 697554 | PILKINGTON OPTICAL | LAC697554B | 2002 | I | 5MM | ----- | ~<360 (88.2%) | ~365 | ~>1000 (99.5%) | 730 | 53 | 3.75 | 0.136 | ||
| 697554 | SCHOTT GLASS TECH. | LaKN14 | 1992 | H / I | 5MM | ~<280(12%) | ~<310 | ~346 | ~>1970.1 (98.1%) | 600 | 734 | 55 | 3.63 | 0.131 | |
| 697554 | SCHOTT GLASS TECH. | NLAK14 | 2000 | P | 10MM | ~<290 (4%) | ~320 | ~361 | ~>1970 (95.0%) | 730 | 55 | 3.63 | 0.131 | ||
| 697555 | HIKARI GLASS CO. | E-LAK14 | 2001 | EG/P | 10MM | ~<280(1%) | ~329 | ~365 | ~>2000(96.2%) | 632 | 686 | ----- | 3.55 | 0.129 | |
| 697555 | HOYA CORP. | LaC14 | DERIVED | HYPOTHETICAL | 1MM* | ----- | ~<280 (63.1%) | ~308 | ~>1550 (99.9%) | 690 | 59 | 3.67 | 0.133 | ||
| 697555 | HOYA CORP. | LaC14 | 1998 | P | 5MM | ~<280 (9%) | ~301 | ~342 | ~1550 (99.7%) | 690 | 59 | 3.67 | 0.133 | ||
| 697555 | OHARA CORP. | LAL14 | 1990 | H / I | 10MM | ~<290 (2%) | ~333 | ~369 | ~>700 (99.7%) | 660 | 57 | 3.70 | 0.134 | ||
| 697555 | OHARA CORP. | S-LAL14 | 1996 | P/EG | 10MM | ~<280 (3%) | ~326 | ~364 | ~>2000 (95.4%) | 660 | 57 | 3.70 | 0.134 | ||
| 697561 | HOYA CORP. | LaC15 | 1978 | H / I | 5MM | ----- | ----- | ----- | ----- | 670 | ----- | 3.95 | 0.143 | ||
| 697562 | CHINA | LAK12 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 620 | 57 | 3.70 | 0.134 | ||
| 697562 | CORNING-FRANCE | C97-56 | 1991 | P | 10MM | ~<280 (19.6%) | ~318 | ~360 | ~>1800 (98.2%) | ----- | ----- | ----- | 3.75 | 0.136 | |
| 697562 | PILKINGTON OPTICAL | LAC697562 | 1990 | H / I | 10MM | ----- | ~<360 (83.1%) | ~373 | ~>1000 (99.3%) | ----- | 62 | 3.78 | 0.137 | ||
| 697564 | PILKINGTON OPTICAL | LAC697564 | 1990 | H / I | 10MM | ----- | ----- | ----- | ----- | 710 | 62 | 3.78 | 0.137 | ||
| 697564 | SCHOTT GLASS TECH. | LaK31 | 1992 | I | 5MM | ~<310 (11%) | ~324 | ~356 | ~>1970.1 (94.5%) | 610 | ----- | 57 | 3.68 | 0.133 | |
| 697565 | OHARA CORP. | LAL64 | 1990 | H / I | 10MM | ~<290 (2%) | ~336 | ~374 | ~>700 (99.8%) | 640 | 58 | 3.67 | 0.133 | ||
| 698386 | SCHOTT GLASS TECH. | BaSF13 | 1992 | I | 5MM | ~<365.0 (32%) | ~371 | ~400 | ~>2325.4 (94%) | 450 | ----- | 71 | 3.97 | 0.144 | |
| 699301 | CHINA | ZF11 | 1996 | H / I | ----- | ----- | ----- | ----- | ----- | 380 | 76 | 4.06 | 0.147 | ||
| 699301 | CORNING-FRANCE | C99-30 | 1991 | P | 10MM | ~<350 (2%) | ~372 | ~393 | ~>1800 (97.6%) | ---- | 578 | 79 | 4.16 | 0.151 | |
| 699301 | EAST GERMANY | SF15 | PRE 1992 | ACQ. BY SCHOTT | 10MM | ~<380 (35.4%) | ~386 | ~414 | ~>1500 (99.4%) | ----- | 87 | 4.07 | 0.147 | ||
| 699301 | HIKARI GLASS CO. | E-SF15 | 2001 | EG/P | 10MM | ~<370(13%) | ~382 | ~418 | ~>2400(90.7%) | 580 | 627 | ----- | 2.97 | 0.108 | |
| 699301 | HOYA CORP. | EFD15 | DERIVED | HYPOTHETICAL | 1MM* | ----- | ~<360 (67.6%) | ~374 | ~>1550 (99.9%) | 545 | 87 | 2.95 | 0.107 | ||
| 699301 | HOYA CORP. | EFD15 | 1998 | P/EG | 5MM | ~<360 (15%) | ~370 | ~390 | ~>1550 (99.7%) | 545 | 87 | 2.95 | 0.107 | ||
| 699301 | HOYA CORP. | FD15 | DERIVED | HYPOTHETICAL | 1MM* | ----- | ~<360 (67.6%) | ~372 | ~>1550 (99.9%) | 395 | 82 | 4.17 | 0.151 | ||
| 699301 | HOYA CORP. | FD15 | 1998 | P | 5MM | ~<360 (15%) | ~369 | ~388 | ~>1550 (99.8%) | 395 | 82 | 4.17 | 0.151 | ||
| 699301 | OHARA CORP. | PBM35 | 1990 | I | 10MM | ~<370 (11%) | ~382 | ~404 | ~>700 (99.8%) | 420 | 74 | 4.10 | 0.148 | ||
| 699301 | OHARA CORP. | S-TIM35 | 1996 | P/EG | 10MM | ~<370 (14%) | ~381 | ~412 | ~>2200 (94.2%) | 500 | 75 | 2.96 | 0.107 | ||
| 699301 | PILKINGTON OPTICAL | EDF699301 | 1990 | H / I | 10MM | ----- | ~383 | ~407 | ~>1000 (99.8%) | 430 | 85 | 4.04 | 0.146 | ||
| 699301 | PILKINGTON OPTICAL | EDF699301A | 2002 | EG | 5MM | ----- | ~<370 (62.4%) | ~395 | ~>2200.0 (96.3%) | 402 | 79 | 4.05 | 0.147 | ||
| 699301 | SCHOTT GLASS TECH. | SF15 | 2000 | P | 10MM | ~<365 (4%) | ~379 | ~399 | ~>1970 (96.3%) | 420 | ----- | 79 | 4.06 | 0.147 | |
| 699302 | SCHOTT GLASS TECH. | NSF15 | 2000 | EG | 10MM | ~<365 (4%) | ~379 | ~408 | ~>1970 (95.4%) | 610 | 80 | 2.92 | 0.106 |